E 200 Repair welding procedures

201.Repair welding shall be qualified by a separate weld repair qualification test.

202.Preheat for repair welding should be minimum 50°C above minimum specified preheat for production welding.

203.When a heat treated pipe or component is repaired by welding, a new heat treatment may have to be included in the qualification of the weld repair procedure, depending on the effect of the weld repair on the properties and microstructure of the existing weld and base material.

204.Qualification of repair welding procedures shall be made by excavating a groove in an original weld welded in accordance with a qualified welding procedure.

شیار حفر شده باید طول کافی برای بدست آوردن تعداد مورد نیاز نمونه‌های آزمایشی + 50 میلی‌متر در هر انتها را داشته باشد.

205.The excavated groove shall be of sufficient length to obtain the required number of test specimens + 50 mm at each end.

Repeated repairs

206.If repeated weld repairs are permitted or agreed, these shall be qualified separately.

207.In case of repeated repairs, the test piece shall contain a repair weld of a qualified repaired original weld. For repeated in-process root repair, single pass cap repair and/or single pass root sealing repairs the repair weld shall be removed prior to re-repair.

Qualification welding

208 .The qualification test shall be made in a manner realistically simulating the repair situation to be qualified. 

209.Qualification welding shall be performed in accordance with E101 through E108.

210.For pipeline girth welds the repair qualification welding shall be performed in the overhead through vertical positions.

211.For roll welding the length of the repair weld may be centred at the 12 o’clock location for external repairs and at the 6 o’clock location for internal repairs, in which case repair welding is qualified for repair welding in these locations only.

Sizing 6dB or 20dB Drop

زمانیکه اندازه ناپیوستگی بزرگتر از قطر ترانسدیوسر باشد، طول ناپیوستگی با قانون ۶  دسی بل قابل اندازه گیری است. اسکن می کنیم تا ماکزیمم ارتفاع را از عیب بگیریم و دامنه را به ۸۰ درصد میرسانیم و به سمت راست اسکن می کنیم و هر موقع که ارتفاع سیگنال به ۴۰ درصد رسید پروب را برداشته و محل مرکز پروب را بر روی قطعه کار مارک میکنیم و دوباره حالت قبلی را تکرار می کنیم اما این بار به سمت چب اسکن می کنیم و ارتفاع به ۸۰ درصد میرسد و با اسکن کردن به سمت متضاد ارتفاع اکو به ۴۰ درصد خواهد رسید باز این محل را در مرکز پروب مارک میکنیم و دو نقطه بدست آمده را به هم  میکنیم و طول عیب بدست خواهد آمد.

DNV-OS-F101

Contact surface

325 For ultrasonic testing the contact surface shall be clean and smooth, i.e. free from dirt, scale, rust, welding spatter, etc. which may influence the result of the testing. Correction for differences in surface conditions and attenuation between the reference block and the actual work piece shall be performed and the maximum correction allowed on flat surfaces is 6 dB.

The Reference notch shall be 1mm wide, rectangular with depth of 1mm . This technique applies only for thickness range 8mm  u t<15mm and fr beam angles W 70°.

E8018-B2, the "B" indicates that the electrode contains certain alloying elements such as chromium (Cr), molybdenum (Mo), and boron (B). These elements contribute to the low-alloy steel's strength and toughness, making it suitable for applications requiring high strength and impact resistance.

8018-C1 is a low alloy, low hydrogen, iron powder electrode designed to weld 2% nickel steels in the 70-80,000 psi range and where low temperature, impact properties must be good. This electrode provides a stable arc in flat and horizontal fillet welding positions, producing weld deposits with fine bead appearance, free from undercuts and with excellent mechanical properties. 8018-C1 may be used with AC or DC (reverse polarity).

بازرسی جوش به روش UT و حد پذیرش

یک استاد دانشگاه درباره اقدام اخیر متروی تهران نوشت: برگزاری مسابقه نامه خودمونی به خدا از سوی مترو کار خوبی است اما بهتر است در کنار این اقدامات که مسجد محل هم می تواند انجام دهد، بخش اجتماعی مترو به کارهای اصلی خود بپردازد. ایجاد نارضایتی و ناراحتی هنر نیست.

بکارگیری اتباع خارجی بدون پروانه کار در مشاغل حوزه سلامت از قبیل مواد غذایی و بهداشت و درمان (رستوران، آشپزخانه، درمانگاه، داروخانه و ...) ممنوع است.

معاونت اجتماعی و پیشگیری از وقوع جرم دادگستری استان تهران 

شروط غیرقانونی در قرارداد کار چه هستند؟

شروط غیرقانونی در قرارداد کار، به توافقاتی گفته می‌شود که برخلاف قوانین آمره کار تنظیم شده‌اند و حتی در صورت رضایت کارگر، فاقد اعتبار قانونی هستند. یکی از مهم‌ترین نمونه‌های این شروط، تعیین ساعت کاری بیش از ۴۴ ساعت در هفته است که با قانون کار مغایرت دارد. همچنین گاهی کارفرما برای خود حق فسخ یک‌طرفه قرارداد را با تعیین مدت زمان مشخصی، مانند ۴۵ روز، قائل می‌شود که این شرط نیز برخلاف اصول قانونی روابط کار است.

از دیگر مصادیق شروط غیرقانونی می‌توان به تبعیض‌های جنسیتی در مزایای شغلی اشاره کرد؛ برای مثال، محروم کردن کارکنان زن از دریافت حق اولاد یا حق تأهل، امری غیرقانونی محسوب می‌شود. در برخی قراردادها نیز توافق می‌شود که مبلغ عیدی کمتر از میزان تعیین‌شده توسط قانون پرداخت شود یا دستمزد کارگر کمتر از حداقل دستمزد مصوب وزارت کار تعیین گردد که هر دو مورد باطل و فاقد اعتبار هستند.

Three types of seismic waves: 

(a) Rayleigh wave  ( Surface wave )

(b) compressional wave ( longitudinal wave )

(c) shear wave

Q30. During ultrasonic inspection (UT) on a 20 mm thick weld, an indication having length 2 mm observed, which is characterised as lack of fusion between the base metal and weld metal. As per the acceptance criteria in ASME Section VIII Division 1, this defect is: 

Not Acceptable

Acceptable

Acceptance depends upon the depth of flaw

None of above

(Explanation: According to ASME Section VIII Division 1, any indication characterized as a lack of fusion is unacceptable regardless of its size. Since the 2 mm long indication in the 20 mm thick weld has been characterized as lack of fusion, it would be unacceptable per ASME Section VIII Division 1 criteria, regardless of its size or depth

The angle at which 90° refraction of a longitudinalsound wave is reached is called the:

a. angle of incidence.

b. first critical angle.

c. angle of maximum reflection.

d. second critical angle.

When inspecting aluminum by the immersion method using water for a couplant, the following information is known: velocity of sound in water = 1.49 × 105 cm/s, velocity of longitudinal waves in aluminum = 6.32 × 105 cm/s, and angle of incidence = 5°. The angle of refraction for longitudinal waves isapproximately:

a. 22°

b. 18°

c. 26°

d. 16°

Sin5/x = 1.49 / 6.32

Beam divergence ( spread out ) is a function of the dimensions of the crystal and the wavelength of the beam transmitted through a medium, and it:

a. increases if the frequency or crystal diameter decreases.

b. decreases if the frequency or crystal diameterdecreases.

c. increases if the frequency increases and crystaldiameter decreases.

d. decreases if the frequency increases and crystaldiameter decreases.

The indication on the instrument display that represents the far boundary of the material being tested is called:

a. grass or hash.
b. the initial pause.
c. the main bang.
d. the back-surface reflection.

Moving a transducer over a test surface either manually or automatically is referred to as:

a. scanning.
b. attenuating.
c. angulating.
d. resonating.

A term  اصطلاحی که used in ultrasonics to express the rate at which sound waves pass through various substances is:

a. frequency.
b. velocity.
c. wavelength.
d. pulse length.

When the motion of the particles حرکت ذرات یک محیط  of a medium is transverse to the direction of propagation, the wave being transmitted is called a:

a. longitudinal wave.

b. shear wave.

c. surface wave.

d. lamb wave.

The boundary between  مرز بین two different materials دو ماده متفاوت  that are in contact with each other is called:

a. a rarefactor.
b. a refractor.
c. an interface.
d. a marker.

For discontinuity geometries other than flat, the echo amplitude دامنه اکو is usually from that observed _________ for a flat discontinuity, of similar orientation perpendicular to the sound beam.

a. identical

b. increased

c. decreased

d. elongated

To evaluate discontinuities that are oriented at anangle to the entry surface so that the sound beam strikes the plane of the discontinuity at right angles,the operator must:

a. change the frequency.

b. grind the surface.

c. angulate the transducer.

d. increase the gain.

In immersion testing, to remove the second water reflection from between the entry surface signal and the first back reflection, you should:

a.increase the repetition rate.

b.decrease the frequency.

c.decrease the sweep length.

d. increase the water path.

If a discontinuity is oriented at an angle other than90° to the sound beam, the results may be a:

a. loss of signal linearity.

b. loss or lack of signal reflected from thediscontinuity.

c. focusing of the sound beam.

d. loss of interference phenomena.

The change in direction of an ultrasonic beam whenit passes from one material to another material inwhich elasticity and density difer is called:

a.reflection 

b.rarefaction

c.angulation.

d.refraction.

In inspecting a 102 mm (4 in.) diameter threadedsteel cylinder for radial cracks extending from theroot of the threads, it would be preferable to transmit:

a.shear waves at an angle to the threads.

b.longitudinal waves from the end of the cylinder and perpendicular to the direction of the threadroots.

c. surface waves perpendicular to the thread roots.

d. shear waves around the circumference of the cylinder.

The distance from a given point on an ultrasonic wave to the next corresponding point is referred to as:

a. frequency.

b. wavelength.

c. velocity.

d. pulse length.

A testing technique in which the crystal or transducer is parallel to the test surface and ultrasonic waves enter the material being tested in a direction perpendicular to the test surface is:

a. straight beam testing.

b. angle beam testing.

c. surface wave testing.

d. lamb wave.

Which one of the following frequencies wouldprobably result in the greatest ultrasonic attenuationlosses?

a.1 MHz

b.2.25 MHz

c.10 MHz

d.25 MHz

"c" – Attenuation factor is attained by subtracting 1 inch (25mm) from the sound – path distance and multiplying the remainder by ⁰. The factor shall be rounded out to the nearest dB value.

Attenuation = (Sound path – 1 ) x 2

= ( 102.34/25.4(1") - 1" ) × 2 = 6 dB

- Indication Rating D

Indication dB ( A ) at 100% FSH ( Full Screen Height ) ( Max ) : 52 dB

Drop to 50% = 6 dB Drop ( افت ) 

D = A - B - C

A = 52 - 6 = 46

D = 46 - 48 - 6

D = - 8 dB

ASME B 31.1 – Power Piping – Ultrasonic Testing .

Welds that are shown by ultrasonic examination to have discontinuities that produce an indication greater than 20% of the reference level shall be investigated to the extent that ultrasonic examination personnel can determine their shape, identity, and location so that they may evaluate each discontinuity for acceptance in accordance with (B.1) and (B.2) below.

(B.1) Discontinuities evaluated as being cracks, lack of fusion,. or incomplete penetration are unacceptable regardless of length.

(B.2) Other discontinuities are unacceptable if the indication exceeds the reference level and their length exceeds the following:

(B.2.1) ¼” (6.0 mm) for t up to ¾” (19.0 mm).

(B.2.2) 1/3 t for t from ¾” (19.0 mm) to 2 ¼ “ (57.0 mm).

(B.2.3) ¾”. (19.0 mm) for t over 2¼” (57.0 mm)

Where t is the thickness of the weld being examined. If the weld joins two members having different thicknesses at the weld, t is the thinner of these two thicknesses

Or, HSD = T X Tan Ø

Similarly, FSD = 2T X Tan Ø

And, 1-1/2 Skip Distance = 3T X Tan Ø

Slag Inclusion 

LEG 2

T : 0.625 INCH

SOUND PATH (SA) : 1.736 INCH

DISTANCE FROM ZERO : 1.504

SA1+SA2=1.736

DEPTH : 0.382

POROSITY

SIZING

Piping isometric elbow degree calculation

یک استاد دانشگاه درباره اقدام اخیر متروی تهران نوشت: برگزاری مسابقه نامه خودمونی به خدا از سوی مترو کار خوبی است اما بهتر است در کنار این اقدامات که مسجد محل هم می تواند انجام دهد، بخش اجتماعی مترو به کارهای اصلی خود بپردازد. ایجاد نارضایتی و ناراحتی هنر نیست.

بکارگیری اتباع خارجی بدون پروانه کار در مشاغل حوزه سلامت از قبیل مواد غذایی و بهداشت و درمان (رستوران، آشپزخانه، درمانگاه، داروخانه و ...) ممنوع است.

معاونت اجتماعی و پیشگیری از وقوع جرم دادگستری استان تهران 

شروط غیرقانونی در قرارداد کار چه هستند؟

شروط غیرقانونی در قرارداد کار، به توافقاتی گفته می‌شود که برخلاف قوانین آمره کار تنظیم شده‌اند و حتی در صورت رضایت کارگر، فاقد اعتبار قانونی هستند. یکی از مهم‌ترین نمونه‌های این شروط، تعیین ساعت کاری بیش از ۴۴ ساعت در هفته است که با قانون کار مغایرت دارد. همچنین گاهی کارفرما برای خود حق فسخ یک‌طرفه قرارداد را با تعیین مدت زمان مشخصی، مانند ۴۵ روز، قائل می‌شود که این شرط نیز برخلاف اصول قانونی روابط کار است.

از دیگر مصادیق شروط غیرقانونی می‌توان به تبعیض‌های جنسیتی در مزایای شغلی اشاره کرد؛ برای مثال، محروم کردن کارکنان زن از دریافت حق اولاد یا حق تأهل، امری غیرقانونی محسوب می‌شود. در برخی قراردادها نیز توافق می‌شود که مبلغ عیدی کمتر از میزان تعیین‌شده توسط قانون پرداخت شود یا دستمزد کارگر کمتر از حداقل دستمزد مصوب وزارت کار تعیین گردد که هر دو مورد باطل و فاقد اعتبار هستند.

Slope 5/100

B=90 Degree

A=87.14 Degree

Distance : 505.18mm