P نامبر متریال فولادهای آلیاژی A335-P9 و A335-P11 و A335-P22

ASME IX ( سکشن ۹ )  برای کاهش تعداد WPS و PQR برای فلزات مختلف P NO تعریف کرده است.

P نامبر 5B 

A335-P9 : ( P NO.5B )

P9 Pipe Chemical Requirements

• Carbon - 0.15% max
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.25% - 1.00%
• Chromium - 8.00% - 10.00%
• Molybdenum - 0.90% - 1.10%

P9 Pipe Specifications

• Tensile strength, min, PSI, (MPa) – 60,000 (415)
• Yield Strength, min, (MPa) – 30,000 (205)

8018-B8 is designed to weld 9% Cr - 1% Mo creep resisting steels such as ASTM A213-T9 and A335-P9. These steels are used in pressure vessels and piping

SFA 5.5 ( Spec for low-alloy steel for smaw )

P نامبر 4 

According to QW/QB – 420 of ASME BPVC Section IX, ASTM A335 Gr. P11 (UNS K11597) is designated with P-number of 4 and Group number of 1.

A335-P11 : ( P NO.4)

P11 Pipe Chemical Requirements

• Carbon - 0.05% - 0.15%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon – 0.50% - 1.00%
• Chromium - 1.00% - 1.50%
• Molybdenum - 0.44% - 0.65%

P11 Pipe Specifications

• Tensile strength, min, PSI, (MPa) – 60,000 (415)
• Yield Strength, min, (MPa) – 30,000 (205)

Before the welding of ASTM A335 P11 pipes, the welding electrodes shall be carefully preheated at the temperature of 300~350°C for 1 hour and the preservation temperature is 80~120°C.

P نامبر  5A

A335-P22 : ( P NO.5A )

P22 Pipe Chemical Requirements

• Carbon - 0.05% - 0.15%
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.50%
• Chromium - 1.90% - 2.60
• Molybdenum - 0.87% - 1.13%

ASME سکشن 9 یا IX بخش D ( متریال ) جدول A1

P نامبر متریال زیر 5B است یعنی حاوی حدوداً ۵ درصد کروم و ۰.۵ درصد مولیبدن است

P5 Pipe Chemical Requirements

• Carbon - 0.15% max
• Manganese - 0.30% - 0.60%
• Phosphorus, max - 0.025%
• Sulfur, max - 0.025%
• Silicon, max – 0.50%
• Chromium - 4.00% - 6.00%
• Molybdenum - 0.45% - 0.65%

P5 Pipe Specifications

• Tensile strength, min, PSI, (MPa) – 60,000 (415)
• Yield Strength, min, (MPa) – 30,000 (205)

مولیبدن در فولاد سختی، استحکام، دوام برندگی، سختی پذیری، استحکام کششی و خزشی را افزایش ولی انبساط پذیری، قابلیت جوشکاری فولاد را کاهش می‌دهد.