مقادیر استحکام تسلیم مواد در Asme سکشن ii جدول Y-1

Table Y-1

(f) The values in this Table may be interpolated to determine values for intermediate temperatures. The values at intermediate temperatures shall be rounded to the same number of decimal places as the value at the higher temperature between which values are being interpolated. The rounding rule is: when the next digit beyond the last place to be retained is less than 5, retain unchanged the digit in the last place retained; when the digit next beyond the last place to be retained is 5 or greater, increase by 1 the digit in the last place retained

قانون گرد کردن رو ذکر کرده که اگر رقم بعد از اون نقطه اعشار کمتر از ۵ باشه تغییری نداره ولی اگر بیشتر از ۵ باشه یک واحد اضافه میشه

See : Asme B16.5  ANNEX B 

METHOD USED FOR ESTABLISHING

PRESSURE–TEMPERATURE RATINGS1  

Material  : SA105

Yield from table Y-1 at 40 Celcius =248Mpa

Yield from table Y-1 at 65 Celcius =233Mpa

Yield from table Y-1 at 65 Celcius =227Mpa

همانطور که در تصویر بالا مشاهده می فرمائید در Minimum value مقدار استحکام تسلیم در ۹۳ درجه سانتیگراد ۲۲۸ مگاپاسکال قید شده با توجه به افزایش دما استحکام تسلیم نیز کمتر می شود.

Annex B Asme b16.5

using 60%OfYs

Flange Class 300#

Yield Sa-105 at 48 Celcius :243.2Mpa

Working Pressure = 50.3 Bar

Yield Sa-105 at 93 Celcius :228.2Mpa...229Mpa

Working Pressure =46.944 Bar

Yield Sa-105 at 95 Celcius :227.857Mpa ... 228Mpa

Working Pressure =46.903 Bar

Yield Sa-105 at 105 Celcius :226.2Mpa

Working Pressure =46.53/ 46.5  Bar

Yield Sa-105 at 140 Celcius :220.6Mpa

Working Pressure =45.38/ 45.4 Bar

ماکزیمم فشار کاری در اتصالات فلنجی کلاس ۳۰۰ پوند طبق زیر ۷۷ بار عنوان شده ... ۱.۵ برابر فشار کاری این کلاس در دمای اتاق ( ۳۸ درجه )( در جدول B16.5 قید شده )

Test Pressure for flanged fittings(300#) : 77 Bar